Dimensions
 Parameter
 Range
 Standard
 Tolerance
Thickness (mm)
0.16 — 4.00
  -
for 0.16 to 0.29 +/-0.01
 for 0.30 to 0.71 +/-0.05
 for 0.72 to 1.40 +/-0.08
 for 1.41 to 2.00 +/-0.11
 for 2.01 to 4.00 +/-0.12
Width (mm)
50 — 1620
914, 1219, 1525
 Slit coil: +2, -0
I.D (mm)
508, 203
-
-
Coil density (kg/mm)
6 max
-
-
Stucco embossed coils are also available in the thickness range of 0.30 — 1.10 mm.
Mechanical properties
Alloy (AA)
Temper 
UTS (mpa)
%E (min)
(50mm gauge length)
Min
Max
0.50 — 0.80 mm
0.80 — 1.30 mm
1.30 — 2.6 0mm
2.60 — 4.00 mm
1050
O
55
95
22
25
29
30
1050
H14
95
125
4
5
6
6
1050
H18
125
  -
3
3
4
4
1070
O
  -
95
27
27
29
34
1070
H14
95
120
4
5
6
7
1070
H18
120
 -
3
3
4
4
1200, 1100
O
70
110
20
25
29
30
1200, 1100
H14
105
140
3
4
5
5
1200, 1100
H16
125
150
2
3
4
4
1200, 1100
H18
140
  -
2
2
3
3
3103, 3003
O
90
130
20
23
24
24
3103, 3003
H14
130
180
3
4
5
5
3103, 3003
H16
150
195
2
3
4
4
3103, 3003
H18
170
-
2
2
3
3
3105
O
95
145
14
14
15
16
3105
H14
150
200
4
4
5
5
3105
H16
175
215
2
2
3
4
3105
H18
195
 -
1
1
1
2
8011
O
85
120
20
23
25
30
8011
H14
125
160
3
4
5
5
8011
H16
150
180
2
3
4
4
8011
H18
175
 -
2
2
3
3
Chemical composition
Alloy (%)
AA 1050
AA 1200
AA 3003
AA 3103
AA 3105
AA 8011
Fe
0.40
1.00
0.70
0.70
0.70
0.60 — 1.00
Si
0.25
(Fe + Si)
0.60
0.50
0.6
0.50 — 0.90
Mg
-
-
 -
0.30
0.20 — 0.80
0.05
Mn
0.05
0.05
1.0 — 1.50
0.9 — 1.50
0.30 — 0.80
0.20
Cu
0.05
0.05
0.05 — 0.20
0.10
0.30
0.10
Zn
0.05
0.10
0.10
0.20
0.25
0.20
Ti
0.03
0.05
0.1 (Ti + Zr)
0.1 (Ti + Zr)
0.10
0.08
Cr
 -
 -
 -
0.10
0.10
0.05
Each (others)
0.03
0.05
0.05
0.05
0.05
0.05
Total (others)
  -
0.125
0.15
0.15
0.15
0.15
Al
99.50
99
Remainder
Remainder
Remainder
Remainder
Single number indicates maximum content
Dimensions
Parameter
Range
Tolerance
Thickness (mm)
  0.3 — 2.00
 for 0.30 to 0.71 +/-0.05
 for 0.72 to 1.4 +/-0.08
 for 1.41 to 2.00 +/-0.11
Width (mm)
  50 — 1250
  Slit coil: +2, -0
I.D (mm)
  203, 305, 406 for thickness < 0.71
-
406, 508 for thickness > 0.71
Density (kg/mm)
  3.5 max
-
Mechanical properties
Alloy (AA)
Temper
UTS (mpa)
%E (min)
(50mm gauge length)
Min
Max
3004
O
150
200
10
3004
H32
193
240
1
3004
H34
220
260
1
3004
H36
240
280
1
3004
H38
260
  -
1
5005
O
103
144
12
5005
H32
117
158
3
5005
H34
137
180
2
5005
H36
158
200
1
5005
H38
180
 -
1
5052
O
170
210
14
5052
H32
210
260
4
5052
H34
230
280
3
5052
H36
255
300
2
5052
H38
268
 -
2
5251
O
160
200
13
5251
H32
190
230
3
5251
H34
210
250
3
5251
H36
230
270
3
5251
H38
255
 -
2
Chemical composition
Alloy (%)
AA 3004
AA 5005
AA 5052
AA 5251
Fe
0.70
0.70
0.40
0.50
Si
0.30
0.30
0.25
0.40
Mg
0.80 — 1.30
0.50 — 1.10
2.20 — 2.80
1.80 — 2.40
Mn
1.00 — 1.50
0.20
0.10
0.10 — 0.50
Cu
0.25
0.20
0.10
0.15
Zn
0.25
0.25
0.10
0.15
Ti
-
-
-
0.15
Cr
  -
0.10
0.15 — 0.35
0.15
Each (Others)
0.05
0.05
0.05
0.05
Total (Others)
0.15
0.15
0.15
0.15
Al
Remainder
Remainder
Remainder
Remainder
Single number indicates maximum content
 
Copyright © Pankaj Metal Corporation